Beta Barium Borate – BBO Crystals SKU: BBO-610H
Beta Barium Borate (BBO) is a nonlinear optical crystal with a combination of unique features: • Wide transparency region • Broad phase-matching range • Large nonlinear coefficient • High damage threshold • Wide thermal acceptance bandwidth • High optical homogeneity …
Variant specifications
| Product | Value |
|---|---|
| Shape Type | Square |
| Width | 6 mm |
| Width Upper Tolerance | 0.1 mm |
| Width Lower Tolerance | -0.1 mm |
| Height | 6 mm |
| Height Upper Tolerance | 0.1 mm |
| Height Lower Tolerance | -0.1 mm |
| Thickness | 0.2 mm |
| Thickness Tolerance Lower Limit | 0.02 mm |
| Thickness Tolerance Upper Limit | -0.02 mm |
| Applications | THG |
| Pump Wavelength | 800 nm - 800 nm |
| Mounted | True |
| Material Type | Crystalline Material |
| Material | BBO |
| Product Type | T1 |
| Theta Angle | 44.3 Deg |
| Theta Angle Tolerance | 0.5 Deg |
| Phi Angle | 90 Deg |
| Phi Angle Tolerance | 0.5 Deg |
| TWD, fringes @633 nm | -(0.25) |
| Parallelism, angle | 0 deg 0 min 0 sec - 0 deg 0 min 20 sec |
| Surface 1 | Value |
|---|---|
| Surface Shape | Plano |
| Surface quality, grind or polish | Polished |
| Power and Irregularity, fringes @633 nm | -(0.25) |
| Clear Aperture, % | 90 % - 100 % |
| Surface 1, Wavelength 1 | Value |
|---|---|
| Coating | P |
| Wavelength | 400 nm - 800 nm |
| AOI (angle of incidence) | 0 deg 0 min 0 sec - 0 deg 0 min 0 sec |
| LIDT | >200 GW/cm², 133 fsec pulse, 800 nm typical, 50 Hz |
| Surface 2 | Value |
|---|---|
| Surface Shape | Plano |
| Surface quality, grind or polish | Polished |
| Power and Irregularity, fringes @633 nm | -(0.25) |
| Clear Aperture, % | 90 % - 100 % |
| Surface 2, Wavelength 1 | Value |
|---|---|
| Coating | P |
| Wavelength | 266 nm - 266 nm |
| AOI (angle of incidence) | 0 deg 0 min 0 sec - 0 deg 0 min 0 sec |
| Side Surface 1 | Value |
|---|---|
| Perpendicularity | 0 deg 0 min 0 sec - 0 deg 5 min 0 sec |